Polymer wear-resistant layer

Polymer wear-resistant layer, also known as
Industrial repair agent, also known as wear-resistant ceramic coating or ceramic wear-resistant clay, is an adhesive added with special materials and aggregates that is applied to the surface of parts to repair damaged parts or make use of them. An industrial technology that gives the surface special functions of wear resistance, high temperature resistance, and corrosion resistance
Ceramic wear-resistant clay is a patented product of Wuhan Dongzhen Technology Company. It is widely used in power plant fans, coarse and fine powder separators, rotary separators, and smoke The inlet and outlet pipes of coal mills, pulverized coal pipes and other parts are also used in the cement plant raw material system clinker system production equipment. This product has super wear resistance and high temperature resistance, and is very convenient to construct. After shutdown, the equipment can be simply disposed of. The product can be coated, and the equipment can be put into use within one hour after heating and curing. It can also be used without heating. It usually cures within one hour without heating. The wear resistance of this product is close to that of wear-resistant ceramic patches.
Porcelain wear-resistant clay is a high-performance wear-resistant polymer material compounded by high-performance wear-resistant particles
ceramics

modified and toughened heat-resistant resin. It is widely used to repair equipment wear caused by high-temperature erosion, corrosion and cavitation, and is also used to prepare wear-resistant coatings on the surfaces of mechanical parts with wear-resistant and anti-corrosion requirements.
Properties

Excellent wear and anti-corrosion properties

The metal base material has high bonding strength
The surface does not flow, the construction is convenient, and it is harmless to the construction workers. Very high technical requirements
Used for repair and protection in various wear and corrosion conditions
Usage
Surface treatment to roughen the parts to be treated, angle grinder grinding or sandblasting, etc. The roughened surface for cleaning shall be a roughened, dry and fresh substrate surface, and shall be free of oil and dust.
Mix the components evenly according to weight ratio
and use up after
Generally, it is configured while constructing. The maximum amount configured at one time cannot exceed
kilograms. If too much is deployed at one time, the glue will solidify quickly, and it will be partially solidified before it is used up and cannot be used. According to the actual temperature, you can mix more in winter and less in summer. If the temperature is too low, the ingredients can be heated appropriately to reduce the viscosity and facilitate preparation.
The appropriate coating thickness for applying this product is
The mixed material should be applied layer by layer to the area to be repaired. The first layer should be compacted to fully infiltrate it with the base material. After reaching the size, the surface should be smoothed. This material cannot be machined, so care should be taken to control the coating thickness to avoid interference during assembly.
It can be put into use when it is cured
. If the temperature is low, heating or extending the curing time should be used to promote curing. Generally, in winter construction, iodine tungsten lamps can be used at a distance from the coating
for irradiation and curing. temperature.