510 Super Strong Acid Copper Brightener

包装：

桶装

规格：

25kg/桶

.Process features: The coating is extremely bright and has good flexibility
The plating solution has good dispersion ability and excellent leveling ability
The coating has no pinholes and has good corrosion resistance
The plating solution is extremely stable. High, the plating surface is clear and shiny, eliminating fogging
Easy to operate and control, extremely high impurity tolerance, long bath life, low maintenance cost
Super strong acid copper brightener is suitable for the automotive industry (such as aluminum Wheel hubs), plastic plating and conventional hardware workpieces, the effect is particularly good.
.Plating solution composition and operating conditions:
Plating solution composition and process conditions
Scope of application
General cylinder usage

- g/L
/> g/L

- mL/L
mL/L

- mg/L
mg/L
Acid copper bright Agent
- ml/L
ml/L
Copper acid brightener
.ml/L
.ml/L
Copper acid brightener
/> .ml/L
.ml/L
Temperature
℃
-℃
Cathode current density
-Ampere/sq.dm
- Ampere/square decimeter
Anode current density
.Ampere/square decimeter
.Ampere/square decimeter
Anode
Phosphorus copper angle (.3 phosphorus )
Phosphor copper angle (.3 phosphorus)
Voltage
Volts
Volts
Stirring method
Air or mechanical stirring
Air or mechanical stirring

3. Preparation method of plating solution:
Add half of the water to the preparation tank. The content of water used for heating to -℃ should be less than mg/L. Add the required .Stir to dissolve completely.
Add .g/L activated carbon, stir for more than an hour, then use a filter pump to filter the plating solution into a clean electroplating tank, and add water until it is close to the water level.
Slowly add the required amount while stirring vigorously to keep the temperature of the plating solution not exceeding ℃.
After cooling the plating solution to ℃, add or according to the content in the plating solution to make the content reach the standard value.
Finally, add the above various additives, electrolyze with a current of .Ampere/square decimeter for about an hour, and then electroplating can begin.
.Equipment requirements:
Plating tank: a steel tank or plastic tank lined with polyvinyl chloride or other various plastics.
Cooling equipment: If the temperature of the plating solution is too high, it will not only increase the consumption of brightener, but also reduce the brightness of the low potential area, so it is very necessary to equip appropriate cooling equipment.
Circulation filtration: Floating objects in the plating solution such as dust, grease, etc. will cause the coating to be rough, produce pinholes, or reduce the brightness. It is best to use continuous circulation filtration of the plating solution. The filter pump will filter the plating solution within at least one hour. The liquid was filtered four times.