Epoxy modified silicone high temperature resistant paint

桶：

1元

Epoxy modified silicone high temperature resistant paint
Composition: This product is chemically modified by epoxy resin and organic silicon oligomers with active groups. Appearance: light yellow to yellow uniform liquid, containing some organic solvents.
Characteristics and uses:
This paint is a high-performance, high-temperature-resistant paint. After film formation, the film has good sealing properties. This product can withstand high temperatures of up to 10 degrees Celsius (depending on color). No baking equipment is required after construction. It is suitable for all high temperature resistant environments to protect it from corrosion by high temperature, acid, alkali, oil, salt and other corrosive media.
Main technical indicators
Appearance: light yellow to colorless transparent liquid, allowing opalescent light, no mechanical impurities
Paint film appearance: smooth paint film with strong adhesion (circling method) grade
/> Viscosity (coating viscometer) seconds/resistant to -°C, no blistering, no shedding
Drying time: Surface dry resistant to salt water for 3 hours without change
Solid dry resistant to acid, alkali and oil without change for 3 hours
Solid content:
Epoxy value:
Silicone content:
Construction and storage:
,
Before painting, the surface of the object must be sandblasted and rust-free. Level or manual rust removal to Level 3. It is strictly forbidden to bring in moisture during construction. It cannot be mixed with other types of paint (including construction tools).
,
The construction proportioning method is: stir thoroughly and evenly, and then paint after aging for 3 minutes. and used up within hours.
This material is ready for use and cannot be stored for a long time (prepared materials). Unfinished materials must be sealed and stored. Construction should be stopped on rainy days or when the relative humidity is greater than 100%.
,
If the paint is too thick, it can be diluted with special thinner. The product should be stored in a cool and dry place, away from direct sunlight, isolated from fire sources, and away from heat sources.
,
The storage period is twelve months. After the expiration, various technical indicators should be inspected. If the index requirements are met, it can continue to be used.
Packaging specifications: Main paint/barrel curing agent/barrel ratio: